  • Structural characterization of platinum foil for neural stimulating electrodes
    Pečlin, Polona ...
    Objective: The objective of this study was to investigate the structural properties of a cold-rolled platinum foil used to manufacture multi-electrode spiral nerve cuffs. Methods: To attain this ... objective, 0.03-mm-thick cold-rolled platinum foil strips with 99.99 wt% purity were used. The resistivity measurements were made using a 4-point probe technique in which the strips were subjected to dynamic annealing in an argon atmosphere. The stored energy of platinum was recorded in an argon atmosphere using differential scanning calorimetry (DSC). Finally, the microstructure of the strips was investigated by optical microscopy. Results: In the resistivity measurements, a small change is observed at ~280°C. This change could be explained as the partial recovery elicited by the decrease of dislocation density. Above 500°C, a significant decrease in resistivity was recorded, and the decrease reached a maximum at ~750°C. These results are consistent with the recrystallization trend detected in DSC, namely the DSC measurement detected very weak heat release during recrystallization, which was actually accumulated during the cold-working. This exothermal peak occurred in the temperature range 380-800°C.
    Vir: Bio-medical materials and engineering. - ISSN 0959-2989 (Vol. 24, no. 5, Jan. 2014, Str. 1827-1835)
    Vrsta gradiva - članek, sestavni del ; neleposlovje za odrasle
    Leto - 2014
    Jezik - angleški
    COBISS.SI-ID - 31529177
    DOI

vir: Bio-medical materials and engineering. - ISSN 0959-2989 (Vol. 24, no. 5, Jan. 2014, Str. 1827-1835)
loading ...
loading ...
loading ...

Vnos na polico